Reliability and interpretation of the microstructural parameters determined by X-ray line profile analysis for nanostructured materials
Department of Materials Physics, ELTE Eötvös Loránd University, POB 32, 1518, Budapest, Hungary
Received:
27
December
2021
Accepted:
9
April
2022
Published online:
27
April
2022
In this overview, the applicability of X-ray diffraction line profile analysis (XLPA) for the characterization of the microstructure in nanostructured materials is overviewed. The dislocation densities obtained by whole pattern fitting and from the breadth of the diffraction peaks are compared. Both theoretical considerations and experimental evidences prove that the evaluation of the peak breadth solely is not suitable for the determination of the dislocation density. In addition, the microstructural parameters determined by XLPA were compared to the values obtained directly by microscopic methods. It was found that the ratio of the grain size obtained by microscopy and the crystallite size determined by XLPA decreases with the reduction of the grain size in nanomaterials, and below 20 nm, the two values agree within the experimental error. In addition, correlation between the microstructural parameters (e.g., crystallite size and dislocation density) determined by XLPA was not found. It was revealed that bottom–up processing methods can produce similarly high defect density in nanostructured materials as severe plastic deformation (SPD). The influence of stacking fault energy, melting point, and degree of alloying on the microstructure of nanomaterials is discussed in detail.
© The Author(s) 2022
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.